Special features of breaking the welded connections of the ferritic steels

Abstract

Were investigated the special features of breaking the welded joints of the high-temperature (oxidation-resistant) (up to 1100°C) of the ferrite class of steel grade 08X25T steel (X8CrTi25, EN 10028-2) by the executed manual arc welding (111 LST EN 24063) by the electrodes of pearlitic, ferrite and austenitic classes. It is established that in the joints being investigated destruction more fre-quently is observed in the heat-affected zone and it is thin-ner in the weld itself. Breaking of the welded connections executed by the electrodes of pearlitic class more fre-quently had brittle character, is thinner intermediate. Breaking the welded connections executed by austenitic electrodes more frequently had plastic nature, thinner - intermediate.

Atlikti karščiui atsparaus (iki 1100°С) feritinės klasės plieno 08Х25Т (Х8CrTi25, EN 10028-2) jungčių, suvirintų rankiniu lankiniu būdu (111 LST EN 24063) perlitinės, feritinės ir austenitinės klasių elektrodais, tyrimai. Nustatyta, kad tiriamieji sujungimai dažniausiai suyra terminio poveikio srityje, rečiau suyra pati siūlė. Jungtys suvirintos perlitinės klasės elektrodais, dažniausiai suyra trapiai, rečiau suirimas būna tarpinio pobūdžio. Austenitiniais elektrodais suvirintų jungčių suirimas dažniausiai būna plastiškas, rečiau – tarpinio pobūdžio.