The properties of refractory concrete with liquid glass based binder and chamotte aggregates

Abstract

Comparative analysis of physical-mechanical characteristics of concrete with different binders and chamotte aggregates has been carried out. It was determined that cold crushing strength of concrete with complex binders (liquid glass + hardener + alumina cement) after its setting, drying and firing at temperature of (500 – 600) ° C is 1.5 – 3 times higher than of concrete with traditional binder (liquid glass + hardener) and amounts to (28 – 45) MPa. Thermal shock resistance of the concrete has been determined by various methods. Analysis of character of cracks development shows that in concrete with complex binder formation of cracks occurs after higher number of cycles and is of larger extent and with more fragments than in traditional concrete. Possibly it is main reason of high thermal shock resistance of the concrete.

Atlikta betonų (tirtų pagal GOST 20910-90) įtrūkimų plėtros pobūdžio analizė rodo, kad betonuose su kompleksiniu rišikliu įtrūkimų atsiranda po didesnio ciklų skaičiaus ir jų bei atskirų fragmentų susidaro daugiau negu tradiciniame betone. Matyt, tai yra pagrindinė šių betonų didelio terminio patvarumo priežastis. Fragmentinė betono struktūra kompensuoja jo terminį išsiplėtimą ir relaksuoja įtempius. Pagal Termoizoliacijos instituto metodiką atlikti betono terminio patvarumo tyrimai, kai ciklo kaitinimo temperatūra siekė 600 ° C, 800 ° C ir 1000 ° C. Nustatyta, kad, keliant ciklo kaitinimo temperatūrą nuo 600 ° C iki 1000 ° C (t.y. didinant terminio smūgio poveikį), smarkiai mažėja betono santykinis terminis patvarumas (nuo 0,7 – 0,4 iki 0,3 – 0,08). Šie rezultatai rodo, kad betono terminis patvarumas turi būti nustatomas įvairiose temperatūrose, nes praktikoje šilumos agregatų eksploatacinės temperatūros dažniausiai nesutampa su įvairiose terminio patvarumo nustatymo metodikose naudojama fiksuota kaitinimo ciklo temperatūra.