Cr-Ni-Mo plieno suvirintųjų jungčių tyrimas

View/Open
2 COPY STRAIPSNIS.pdf (6.823Mb)
GZAICEVMAGISTR.pdf (27.45Mb)
Author
Zaicev, Georgij
Metadata
Show full item record
Abstract
Baigiamajame darbe nagrinėjama terminio apdorojimo po suvirinimo įtaka feritinio austenitinio plieno suvirintųjų jungčių korozijos atsparumui, stiprumui, smūginiam tąsumui ir kietumui. Baigiamajame darbe nagrinėjama Cr-Ni-Mo plieno suvirintųjų jungčių terminio apdorojimo įtaka mechaninėms savybėms ir atsparumas korozijai. Atlikta dviejų skirtingų (rūšių) dvifazio nerūdijančiojo plieno analizė: „Duplex“ plieno (EN 1.4462) ir „Super duplex“ plieno (EN 1.4410). Esant skirtingoms temperatūroms, nekeičiant kaitinimo trukmės ir skirtingai aušinant, buvo atliekamas terminis apdorojimas po suvirinimo. Atlikti šie bandymai: smūginio tąsumo bandymai, kietumo matavimai pagal Vikerso metodą, ferito kiekio nustatymas, skersinio tempimo bandymai, makrostruktūros ir mikrostruktūros tyrimai. Tyrimais nustatyta, kad abiejų rūšių plieno virintinės jungties korozinis atsparumas po terminio apdorojimo (T = 9000С–9500С) sumažėjo. Taip pat sumažėjo smūginis tąsumas. Baigiamojo darbo apimtis: 58 p. teksto be priedų, 57 iliustr., 12 lent., 13 bibliografinių šaltinių.
 
In Master's final work was analyzed post weld heat treatment modes influence on austenitic ferritic stainless welded joints corrosion resistance and mechanical properties. Analyzed of two different duplex stainless steel: duplex steel (EN 1.4462) and super duplex steel (EN 1.4410). At different temperatures and cooling, without changing of holding time, post weld heat treatment was performed. Tests, that was applied for welded joints and samples were following: impact test, hardness testing, determination of ferrite value, tensile test, macro and micro structure analysis. Investigations showed, that reduced corrosion resistance of both steel grades welded joints after post welding heat treatment (T= 900 0С-950 0С ) It also reduced impact strength. The volume of the thesis: 58 pages without the attachments, 57 illustrations, 12 tables, 13 bibliographical sources.
 
URI
https://etalpykla.vilniustech.lt/handle/123456789/110949
Collections
  • Magistrų darbai / Master theses [2734]

 

 

Browse

All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjects / KeywordsInstitutionFacultyDepartment / InstituteTypeSourcePublisherType (PDB/ETD)Research fieldStudy directionVILNIUS TECH research priorities and topicsLithuanian intelligent specializationThis CollectionBy Issue DateAuthorsTitlesSubjects / KeywordsInstitutionFacultyDepartment / InstituteTypeSourcePublisherType (PDB/ETD)Research fieldStudy directionVILNIUS TECH research priorities and topicsLithuanian intelligent specialization

My Account

LoginRegister