Utilization of mineral wool waste in production of ceramic products

Abstract

During production of mineral wool, the mineral wool centrifuging waste appears in big quantities and its utilization presents an urgent problem. This waste can be effectively used as additive in production of ceramic products. The aim of this study is to investigate the impact of mineral wool melt centrifuging waste on process of formation of ceramic body and its properties. It is established that upon firing of samples at temperature of 1080 o C, it is possible to receive the ceramic body of density 2290 kg/m3 and water absorbtion 1,8 %. The investigation of mechanical properties showed that versus reference sample the compressive strenth increased from 30,7 to 59,7 MPa.

Переработка отходов производства минеральной ваты является актуальной проблемой. В данной работе исследована возможность использования отходов, образующихся при диспергировании расплава центробежным методом, в качестве добавки в производсве керамических изделий на основе легкоплавких глин. Отходы составляют частицы застывшего расплава и минерального волокна. Исследована влияние добавки на процесс спекания и свойства керамики. Установлено, что при обжиге образцов при температуре 1080°С получена керамическая черепица с плотностью 2290 кг/т3, водопоглашением 1,8 %. Использование добавки увеличило предел прочности на сжатие, по сравнению с контрольными образцами, от 30,7 МПа до 59,7 МПа.