Calorimetric investigations of high aluminate cement hydration in the presence of waste oil-cracking catalyst
Santrauka
Aluminosilicate-based zeolitic waste catalyst (fluidized catalytic cracking catalyst, FCCC) is produced by petrochemical industry in the fluidized bed catalytic cracking process. The present work shows that FCCC zeolitic structure undergoes changes after treatment at 1000ºC and is destroyed above 1050°C. Non-treated or high temperature treated FCCC, due to its chemical composition, can be used in refractory cement-based materials as a fine additive. Calorimetric investigation shows that non-treated or treated at 1000°C, FCCC considerably accelerates the hydration of high aluminate (Al2O3>70%) cement due to its zeolitc structure. Aliumosilikatinė ceolitinė atlieka (panaudotas naftos katalizatorius iš katalitinio krekingo įrenginio) dėl savo cheminės sudėties gali būti naudojama ugniai atspariose cementinėse medžiagose. Nustatyta, kad katalizatoriaus atlieką apdorojus 1000°C temperatūroje pasikeičia jos ceolitinė struktūra, o 1050°C temperatūroje ši struktūra suyra. Kalorimetriniai tyrimai parodė, kad dėl ceolitinės struktūros neapdorota arba apdorota 1000°C temperatūroje katalizatoriaus atlieka spartina aliuminatinio cemento, kuriame Al2O3 > 70 %, hidrataciją.