Influence of a technogenic silicate product admixtures on silicate concrete properties

Abstract

The influence of three types of technogenical products (cement dust – waste of cement production, autoclaved cellular concrete waste and condensate from the autoclaves) on silicate concrete properties was analysed in this paper. Use of these products is limited and the condensate is practically unused for production. It was determined that the mixture of water and condensate (1 : 1) could be used to slake the silicate mixture, then the compressive strength of the silicate concrete increases by 15%, and additionally including 3 wt.% of cement dust or 5 wt.% of porous concrete waste, the silicate concrete compressive strength increases from 21 % to 26 %.

Straipsnyje nagrinėjama trijų rūšių technogeninių produktų įtaka silikatbetonio savybėms. Tai cemento dulkės (cemento gamybos atliekos), autoklavinio akytojo betono atliekos bei autoklavuose susidaręs kondensatas. Šie produktai naudojami ribotai, o kondensatas gamyboje iš viso nenaudojamas. Nustatyta, kad panaudojus silikatinei masei gesinti vandens ir kondensato mišinį santykiu 1:1, silikatbetonio gniuždomasis stipris padidėja 15%, o papildomai pridėjus į silikatinį mišinį 3% kietųjų medžiagų masės cemento dulkių arba 5% akytojo betono atliekų, silikatbetonio gniuždomasis stipris padidėja nuo 21 % iki 26 %.