The influence of binding materials composition and fibrous additives on the properties of porous concrete

Abstract

The paper aims to determine the effect of lime/Portland cement ratio in the matrix and basalt wool additive in porous concrete formation mixes on the macro- and microstructure, strength and frost resistance of specimens subjected to volumetric and one-side freezing and thawing. It has been found that porous concrete specimens with lime/Portland cement ratio of 1:1 (according to the equivalent amounts) subjected to volumetric freezing and thawing meet frost resistance standards (for concrete of the grade F 25). Mass losses of specimens with the addition of 0,4 % of basalt fibres made as little as 2% after 25 freeze-thaw cycles, while their compression strength increased. Light-weight porous concrete articles should not be used for one-sided freezing-thawing method. The effect of fibre additives on the micro- and macrostructure is negligible.

Nagrinėjama akytojo betono formavimo mišinių rišamosios medžiagos (kalkių ir portlandcemenčio) santykio ir bazaltinės vatos priedo įtaka bandinio makro- ir mikrostruktūrai, stiprumui ir atsparumo šalčiui šaldant ir šildant tūriniu ir vienpusiu būdais. Nustatyta, kad tūriniu būdu šaldomi ir atšildomi akytojo betono bandiniai, kurių formavimo mišiniuose kalkių ir portlandcemenčio santykis 1:1 (pagal ekvivalentinius kiekius), atitinka akytojo betono standartų atsparumo šalčiui reikalavimus (F 25 markės). Papildomai dar pridėjus 0,4 % bazaltinio pluošto po 25 šaldymo ir atšildymo ciklų masės nuostoliai sudarė tik 2 %, o bandinių stipris gniuždant padidėjo. Vienpusis šaldymo ir atšildymo metodas mažo tankio akytojo betono bandiniams yra netikslingas. Pluoštinio priedo įtaka makro- ir mikrostruktūrai neesminė.