Reliability estimation of the ferritic steels welded joints

Abstract

It was evaluated the reliability of the welded joints of high-temperature oxidation-resistant (up to 1100°С) grade 08Х25Т steel of ferrite class GOST 5632-72 (Х8CrTi25, EN 10028-2) by the manual arc welding (111 LST EN 24063) with the coated electrodes of different classes. Is proposed the method of evaluating the reliability of the welded joints of using maximum hardness of weld material and near-weld zone and the plasticity of structure. It is established that in the connections being investigated the smallest reliability have joints that are welded by the nonfusible electrode, copper (UTP-34N) and pearlitic (UONI-13/45) electrodes, and greatest − by austenitic (UTP-068HH) and austenite-ferrite (UTP-65D) electrodes.

Įvertintas kaitrai atsparaus (iki 1100°С) feritinės klasės plieno 08Х25Т GOST 5632-72 (Х8CrTi25, EN 10028-2) jungčių, suvirintų rankiniu lankiniu būdu (111 LST EN 24063) skirtingų klasių glaistytaisiais elektrodais, patikimumas. Siūloma suvirintųjų jungčių patikimumą vertinti pagal maksimalų siūlės ir terminio poveikio srities metalo kietumą ir struktūros plastiškumą. Nustatyta, kad tiriamuose sujungimuose mažiausiai patikimumas yra jungtys, suvirintos nelydžiuoju elektrodu, bei variniais (UTP-34N) ir perlitiniais elektrodais (UONI-13/45), o patikimiausios – suvirintos nikeliniais (UTP-068HH) ir austenitiniais-feritiniais (UTP-65D) elektrodais.