Structurization of polyamide in dimethylformamide solution

Abstract

Peculiarities of supermolecular structure order (SMO) formation in polyamide (containing asparaginimide cycles) – dimethylformamide (DMF) system at polymer concentrations 5 - 20 g/dl and temperature interval 0 - 60 ° C were investigated. The SMO was characterized by system’s turbidity (t ) and particle mean equivalent radius (). An increase in polymer solution concentration causes an increase in SMO formation rate by an order of 2. The kinetic SMO formation curves possess a two-stage character: the main process, after which follows a slow increase in SMO level. The SMO formation process proceeds at the same temperature as the initial polymer was dissolved. The formed SMO particles melt at 20 ° C temperature when the system is heated. The minimal SMO level melt temperature formation increases with an increase in polymer concentration. All the obtained investigation data indicates towards the SMO crystalline nature of the investigated system.

Matuojant polimero dimetilformamidinio tirpalo optinį tankį (drumstumą), ištirtas poliamido su asparaginmidiniais ciklais želatinėjimo (supermolekulinės tvarkos formavimosi – SMT) procesas. Parodyta, kad, keičiantis polimero koncentracijoms nuo 5 iki 20 g/dl, supermolekulinės tvarkos lygis pakyla 102 laipsniu. Ši tvarka nusistovi toje pačioje temperatūroje, kurioje polimeras buvo ištirpintas. SMT buvo apibūdinamas sistemos drumstumu, t ir vidutiniu ekvivalentiniu dalelės spinduliu,` rl . Temperatūros įtaka polimero dalelių formavimuisi yra ekstremalaus pobūdžio. Kinetinės SMT kreivės formuojasi dviem stadijomis: vyksta pagrindinis procesas, o po jo toliau lėtai paspartėja SMT. Gauti duomenys apie tirtą sistemą leidžia padaryti išvadą, kad sistemos struktūrizavimas yra kristalinės prigimties.