Peculiarities of xonotlite synthesis and formation of thermal -insulating products made from xonotlite

Abstract

The process of xonotlite synthesis has been investigated. The influence of SiO2 component on suspension (C/S = 1, W/S = 30) viscosity and filtration speed, and the influence on admixtures on suspension consistence as well as on bending strength of articles formed from synthesis products have been determined. The possibility of formation of thermal-resistant insulation materials of 1000 °C exploitation temperature, made from xonotlite synthesized by the above method with admixture of approximately 5 % of kaolin wool (dry materials) has been ascertained.

Ištirtas ksonotlito sintezės periodiniu būdu procesas, nustatyta SiO2 komponento įtaka gautos ksonotlito suspensijos (C/S = 1, V/K = 30) klampai ir filtravimosi greičiui, ištirta priedų įtaka suspensijos filtravimosi greičiui bei iš sintezės produktų suformuotų gaminių stipriui lenkiant. Nustatyta, kad iš šiuo būdu susintetinto ksonotlito, pridėjus apie 5 % sausos medžiagos – kaolininės vatos, galima suformuoti termiškai atsparias izoliacines medžiagas, kurios gali būti eksploatuojamos 1000 °C temperatūroje.