Dujų betono su mišria rišančiąja medžiaga formavimo ypatumų tyrimai
Santrauka
Porous concrete is a cheap material produced from local raw materials. That is why, it is important to improve it's properties, especially the product's density. This paper deals with porous concrete made using a mixed binder composition (lime + Portlandcement) formation peculiarities and determination of optimal product formation parameters for 300 - 350 kg/m3 product dependency on the binder mixture composition. A wide density interval (200 - 500 kg/m3 ) was investigated to determine the optimal above mentioned porous concrete density parameters. It was determined, that the porous concrete density with a mixed binder composition has a complex dependency from water and dry solids ratio (V/K, mixed binder composition and amount of Al powder. Mathematical equations of porous concrete density on technological parameter were derrived. It was found that the lime contant increase in the lime- Portlandcement binder mixture, lowers Al powder effectiveness, increases the product's density and decreases the technological operation time duration.