The alkali and temperature resistance of some fibres

Abstract

Porous concrete needs to be reinforced to improve its strength, frost-resistance, durability etc. An alkaline media (pH=12.6) is formed during the production of porous autoclave concrete, so the reinforcing fibres should be stable to alkali and temperature influence (up to 180 oC). The resistance to these factors of four different fibres (mineral and kaolin wool, carbon and polypropene fibres) was investigated using X-ray diffraction and scanning electron microscopy (SEM). It was determined that kaolin wool cannot be recommended for use as a reiforcing agent during the formation of porous concrete. The others investigated fibres might be used for these purposes.

Akytųjų betonų dirbiniai, palyginti su tankiaisiais betonais, turi gana nedidelį lenkiamąjį bei tempiamąjį stiprį ir yra gana trapūs. Dėl to juos gaminant ir transportuojant gali atsirasti defektų, įtrūkimų. Šių trūkumų galima išvengti gaminius armuojant pluoštu. Autoklavinio akytojo betono formavimo mišiniuose susidaro šarminė (pH ~ 12,6) terpė, todėl pluoštinės medžiagos turi būti atsparios šarmų ir temperatūros (iki 180 ° C) poveikiui. Darbe buvo panaudoti mineralinės ir kaolino vatos, anglies bei polipropeno pluoštai, skirtingą laiką išlaikyti skirtingose šarminėse aplinkose (sotieji Ca(OH)2 tirpalai, gauti iš portlandcemenčio bei negesintų kalkių, 0,04 M ir 0,12 M koncentracijos NaOH tirpalai) ir skirtingoje temperatūroje (20 ° C; 50 ° C bei 180 ° C). Nustatyta, kad kaolino vatos pluoštas reaguoja su NaOH tirpalais autoklavinėmis sąlygomis ir sudaro aliumosilikatus, kurių sudėtis artima Na2Al2Si2O8 × H2O cheminei formulei. Pluoštas tampa trapus, todėl akytajam betonui armuoti jis netinka. Atspariausias šiomis sąlygomis yra anglies pluoštas, kuris išlieka beveik sveikas. Kiti pluoštai (polipropenas ir mineralinė vata) yra pažeidžiami iš dalies.