The influence of oil cracking catalyst waste on the properties of refractory castables

Abstract

Fluidized bed catalytic cracking catalyst waste is a zeolite material. Its unique properties are underused in cementitious materials production technology. Various additives, modifiers used in refractory castables are very expensive, so the use of catalyst waste as a modifying additive of castable properties has not only an ecological (waste recycling) but also an economical basis. Medium cement refractory castable was developed using 70 % and 40 % of aluminium oxide containing aluminate cement and catalyst waste additive, respectively 2,5 % and 5,0 %. The work also reveals an efficient effect of catalyst waste on alumina cement hydration, structure formation during cement solidification and after treatment at high temperature.

Naftos krekinge naudotas katalizatorius yra ceolitinė medžiaga, kurios unikalios savybės mažai išnaudojamos cementinių medžiagų gamybos technologijoje. Ugniai atspariuose betonuose naudojami įvairūs priedai-modifikatoriai yra labai brangūs, todėl naudoto katalizatoriaus panaudojimas, kaip modifikuojančio betono savybes priedo, turi ne tik ekologinį (atliekų utilizavimas) bet ir ekonominį pagrindą. Vykdant šį darbą sukurti vidutinio cemento kiekio ugniai atsparūs šamotbetoniai su 70 % ir 40 % aliuminio oksido turinčiais aliuminatiniais cementais ir naudoto katalizatoriaus priedu atitinkamai 2,5 % ir 5,0 %. Darbe taip pat atskleistas efektyvus katalizatoriaus poveikis aliuminatinio cemento hidratacijai, cemento akmens struktūros susidarymui kietėjimo metu ir jos pokyčiams veikiant aukštoms temperatūroms.