Optimisation of Nano-ZnO and Nano-SiO 2 mixing time for bitumen modification

Abstract

Nanotechnologies have gradually penetrated to the field of bitumen modification especially where durable asphalt mixtures have to be designed. Longer mixing time, higher temperatures or/and higher rotation (shearing) speeds are needed to increase the dispersion of nanoparticles in bitumen. However, this is not necessarily beneficial to the physical and mechanical properties of the final material. As a result, in this study nano-zinc oxide (nano-ZnO) and nano-silica (nano-SiO 2 ) mixing time for bitumen modification was optimized considering the physical and mechanical properties of the final bitumen. For this purpose bitumen PMB 25/55-60 was modified with nanoparticles at 180 °C using a laboratory high-shear mixer at a rotation speed of 4000 rpm for different modification time selected on the basis of literature review (60 and 90 minutes). Penetration, softening point, viscosity at 135 °C, recovery and non-recoverable creep compliance (multiple stress creep and recovery test) at 60 °C were measured in order to determine the optimal mixing time. The results showed that 60 minutes ensures the dispersion of nano-ZnO and nano-SiO 2 in the bitumen PMB 25/55-60 and longer mixing time do not have a significant effect on the properties of nano-ZnO and nano-SiO 2 modified bitumen (the difference was less than 7%).